API5L/A106B Seamless Steel Tubes
A106B steel’s chemical composition is similar to that of A53 Grade B and API 5L B. Its carbon content maxes out at 0.3% and its nickel at 0.4%. Its manganese minimum must fall between 0.29% και 1.06%.
Grade B maintains a higher carbon content than grade A but less than grade C. For each reduction of 0.01% of the maximum carbon amoun, manganese may increase 0.06% above the specified value up to a maximum of 1.35%.
The differences in chemistry between A53 and A106 seem minor, but they are important. A53 steel may include silicon, but A106 steel must include at least 0.10% silicon in the alloy. Silicon is an important component in heat resistance ability.
Εάν έχετε ερωτήσεις, please contact sales@tubesolutions.com.cn
A106 steel must be produced with killed steel — a totally deoxidized alloy that features a high degree of chemical homogeneity. In killed steel, no reaction occurs between the carbon and the oxygen during solidification. Consequently, the product is more chemically uniform.
- Περιγραφή
- Εξέταση
Περιγραφή
API5L/A106B Seamless Steel Tubes
Standard: ASTM A106B/API 5L
Seamless carbon steel tubes for high-temperature service
● Application: for high temperature service.
● Size range: O.D.: 15-120mm W.T.: 1-15mm L.: 15000mm max.
Table 1: steel grade and chemical composition:
Grade | C (μέγ.) | Μν | P (μέγ.) | S (μέγ.) | Σι (Λεπτά) | Cr (μέγ.) | Cu (μέγ.) | Mo (μέγ.) | N (μέγ.) | V (μέγ.) |
A | 0.25 | 0.27-0.93 | 0.035 | 0.035 | 0.10 | 0.40 | 0.40 | 0.15 | 0.40 | 0.08 |
B | 0.30 | 0.29-1.06 | 0.035 | 0.035 | 0.10 | 0.40 | 0.40 | 0.15 | 0.40 | 0.08 |
C | 0.35 | 0.29-1.06 | 0.035 | 0.035 | 0.10 | 0.40 | 0.40 | 0.15 | 0.40 | 0.08 |
Table 2: Mechanical property:
Grade | Tensile Strength Rm (Mpa) | Yield Point (Mpa) | Elongation A% | Delivery Condition |
A | ≥330 | ≥205 | 20 | Annealed |
B | ≥415 | ≥240 | 20 | Annealed |
C | ≥485 | ≥275 | 20 | Annealed |
Table 3: Dimension Tolerances:
Pipe Type | Pipe Sizes | Tolerances | |
Cold Drawn | OD | ≤48.3mm | ±0.40mm |
≥60.3mm | ±1%mm | ||
WT | ±12.5% |
A106 steel’s chemical composition is similar to that of A53 Grade B and API 5L B. Its carbon content maxes out at 0.3% and its nickel at 0.4%. Its manganese minimum must fall between 0.29% και 1.06%.
Grade B maintains a higher carbon content than grade A but less than grade C. For each reduction of 0.01% of the maximum carbon amoun, manganese may increase 0.06% above the specified value up to a maximum of 1.35%.
The differences in chemistry between A53 and A106 seem minor, but they are important. A53 steel may include silicon, but A106 steel must include at least 0.10% silicon in the alloy. Silicon is an important component in heat resistance ability.
A106 steel must be produced with killed steel — a totally deoxidized alloy that features a high degree of chemical homogeneity. In killed steel, no reaction occurs between the carbon and the oxygen during solidification. Consequently, the product is more chemically uniform.
Εάν έχετε ερωτήσεις, please feel free to contact us